摘要: 以工业木质素为原料,采用羟甲基化反应提高木质素反应活性,确定了羟甲基化反应木质素和催化剂的最佳配比:木质素与甲醛质量比为3:1、催化剂用量为 0.25%(以木质素原料计),并用FT-IR和 13CNMR 对羟甲基化反应结果进行了分析。通过羟甲基化木质素磺酸盐(HLF)与酚醛树脂(PF)共混制得木质素酚醛树脂(LPF)胶黏剂。实验结果表明,该胶具有制备工艺简单、游离甲醛低的特点,用HLF替代 40% 的PF时,其胶合强度达到国家Ⅰ类胶合板的要求。

Abstract: The lignin-phenol-formaldehyde resin adhesive was prepared by blending modified technical lignin with phenol-formaldehyde resin. Lignin was modified byhydroxymethylation to increase reactivity and the resultedhydroxymethylated lignin was analyzed by FT-IR and 13CNMR. The optimal conditions ofhydroxymethylation are as follows:lignin-formaldehyde mass ratio 3:1, catalyst dosage 0.25%.When 40% of phenol-formaldehyde resin(PF)was replaced byhydroxymethylated lignin, the adhesive thus formulated showed low free formaldehyde, and the bonding strength could meet the standard of type I plywood.